LG Hausys LD2700G/M

LD2700G/M

LD2700G is a calendered PVC vinyl supplied with permanent pressure sensitive adhesive. It’s designed for solvent-based inkjet printing and guarantees up to 2-years outdoor durability. The product is designed to meet high resolution printing with excellent color.

LG Hausys ld2700g

Areas of use

  • Solvent inkjet printing: Vutek, Arizona, Mimaki, Mutoh, Roland, DGI etc..
  • Outdoor display, sign, exhibition stand, etc.
    • The films conform well to flat and seamed surfaces, when processed and applied according to LG Hausys's recommendations.
Advantage
  • 2years durable calendered film
  • Excellent printing performance
  • Dimensional stability and performance under a wide range of physical and climatic conditions
  • Excellent weather resistance: Solvent based acrylic adhesive (Permanent Type)
  • Liner : double side olefin coated paper
Characteristic
Item Description
Film 3.2 mils(80 microns) opaque film with gloss finish
Thickness 4.1 mils(105 microns) with adhesive (± 10 %)
Adhesive Acrylic based pressure sensitive(Solvent based)
Adhesive color Clear
Liner Double side olefin coated paper
Application surfaces Flat, slightly curved surfaces
Application temp. ≥10℃(18 to 25℃ optimum)
Durability

Durability is based on field experience and exposure tests in South Korea. Outdoor durability is 2 years when properly processed and applied (unprinted film vertical exposure).

Shelf Life

Shelf life is 1 year from factory shipment.
Storage condition: Free from excessive moisture, temperature, direct sunlight (20℃ x 50% R.H)

Physical Properties
Property Metric Units Description
Thickness (Including adhesive) 4.1mils(105㎛) ± 10% Micrometer
Tensile strength ≥ 1.8kg/cm² ASTM D882
Elongation ≥ 100% ASTM D882
Peel adhesion(24hrs) ≥1,200g/in 180 peeling PSTC-1
Service temp. range -25℃ ~ 82℃ Film applied Al panels 24hrs prior test
Application temp. ≥ 10℃ 18 to 25℃ optimum, on clean substrate
Opacity Tt ≤ 10 Haze Meter (Tt: Transmission)
Gloss 60 ↑ @60, in Machine Direction
Dimensional Stability Max 0.5mm Adhered to Aluminum Plate, Length Direction
(80℃ Oven, 24hr , Average)
Release liner thickness 0.14mm