LG Hausys LP3912G/M

LP3912G/M

LP3912G/M is a high gloss calendered PVC film for protecting digitally printed image. It provides protection from damaging from UV radiation, scratch and abrasion. Moreover, it offers enhanced colors and durability.

lp3912 i0

Areas of use

  • Solvent inkjet printing: Vutek, Arizona, Mimaki, Mutoh, Roland, DGI etc
  • Indoor and outdoor protection of large format digital image
Advantage
  • Protecting from UV rays, scratch and abrasion
  • Long durable calendered film ( 5years)
  • Excellent printing performance
  • Enhancing color of image
  • Excellent weather resistance : Solvent Based Acrylic Adhesive
  • Standard Width: 30”, 54”, 60”
  • Standard Length: 50yd
Characteristic
Item Description
Film 3.6mils(90㎛) Transparent film with gloss(matte) finish
Thickness 4.7mils(120㎛) with adhesive (± 10 %)
Adhesive Acrylic based pressure sensitive (Solvent based)
Adhesive color Clear
Liner Double sides PE coated paper
Application surfaces Flat, rounding etc
Application temp. 10℃(18 to 25℃ optimum)
Durability

Durability is based on field experience and exposure tests in South Korea. Outdoor durability is 5 years when properly processed and applied (unprinted film vertical exposure)

Accelerated: 2000hr minimum

As determined in an Atlas Weather-o-meter conforming to ASTM G-26-77, section4, using the standard dual cycle of 102minutes of light at 63℃( 145℉) and 18minutes of water spray at 63℃(145℉)

Accelerated: 1000hr minimum

As determined in a QUV weathering tester using UV light(UVB 313 bulbs) at 63℃(145℉)

Shelf Life

Shelf life is 1 year from factory shipment
Storage condition: Free from excessive moisture, temperature, direct sunlight (20℃ x 50% R.H)

Physical Properties
Property Metric Units Description
Thickness (Including adhesive) 4.7mils(120㎛) ± 10% Micrometer
Tensile strength ≥ 1.8kg/cm² ASTM D882
Elongation ≥ 100% ASTM D882
Peel adhesion(24hrs) ≥1,200g/in 180 peeling PSTC-1
Service temp. range -25℃ ~ 82℃ Film applied Al panels 24hrs prior test
Application temp. ≥ 10℃ 18 to 25℃ optimum, on clean substrate
Opacity Tt >85 Haze Meter (Tt: Transmission)
Gloss 60 ↑ @60, in Machine Direction
Matte 10↓ @60, in Machine Direction
Dimensional Stability Max 0.5mm Adhered to Aluminum Plate, Length Direction
(80℃ Oven, 24hr , Average)
Release liner thickness 0.14mm  
Fabrication
Laminating
No heat is required. It can be used most squeeze roll laminators. Keep the film flat during lamination.